DOW RTV-3483 Silicone (20+1)
₹53999(Including all taxes)
DOW SILASTIC RTV-3483 Rubber is a two-part material consisting of SILASTIC RTV-3483 Base, which when mixed with SILASTIC RTV-3083 Curing Agent, cures at room temperature by a condensation reaction. A range of materials can be cast into the cured silicone mold: plaster, polyurethane and polyester resins are materials typically used.
View Technical Data Sheet
Property | Unit | Result |
Base and curing agent mixture (100:5 by weight) |
|
|
Mixed viscosity | mPa.s | 16,000 |
Color |
| White |
Working time of catalyzed mixture at 23C (73.4F), min | minutes | 90-120 |
Curing time, maximum | hours | 24 |
Cured for 2 days at 23C (73.4F) |
|
|
Hardness (Shore A) |
| 13 |
Tensile strength | MPa | 3.9 |
Elongation at break | % | 680 |
Tear strength | kN/m | 25 |
Relative density at 25C (77F) |
| 1.16 |
Linear shrinkage | % | 0.2-0.4 |